Electrochemical Comparative Characteristics of La(Fe,Si)13 Type Materials with Different Content of Co in Acidified Phosphate Environment in Presence of Cl- Ions

Authors

  • Dorota KLIMECKA-TATAR Czestochowa University of Technology
  • Grażyna PAWŁOWSKA
  • Klaudia RADOMSKA
  • Piotr GĘBARA

DOI:

https://doi.org/10.5755/j01.ms.25.3.19536

Keywords:

electrochemical characteristics, pitting corrosion, La(Fe, Si)13, potentiokinetic curves, roughness measurement

Abstract

In the paper the electrochemical characteristics of alloys based on La(Fe,Si)13 phase have been presented. The material for research was the LaFe11.8-xCoxSi1.2 alloy with different cobalt content. Presented electrochemical characteristics provide information about pitting corrosion. This kind of corrosion is one of the most common local corrosion, it is especially undesirable for multi-phase alloys based on rare earth elements, as it contributes to the sudden and unexpected destruction of the surface of the material in working conditions. In the paper the results of potentiokinetic corrosion tests determined for LaFe10.72Co1.08Si1.2 and LaFe11.00Co0.8Si1.2 alloys in acidified phosphate solution (pH = 3) with different addition of chloride ions (Cl-) have been presented. Also analysis of alloys surface before and after corrosion measurement have been presented. The surface analysis have been carried out on the basis of profilometric roughness tests and optical microscopy observation. The studies have shown low resistance of LaFe10.72Co1.08Si1.2 and LaFe11.00Co0.8Si1.2 alloys to pitting corrosion, which, however, increases with Co content increase.

DOI: http://dx.doi.org/10.5755/j01.ms.25.3.19536

Author Biography

Dorota KLIMECKA-TATAR, Czestochowa University of Technology

Adijunct in Depatmet of Production Engineering and Safety, Czestochowa University of Technology, POLAND, UE

Downloads

Published

2019-05-10

Issue

Section

METALS, ALLOYS, COATINGS