Influence of Laundering on the Quality of Sewn Cotton and Bamboo Woven Fabrics

Authors

  • Jurgita KOŽENIAUSKIENĖ Kaunas University of Technology
  • Virginija DAUKANTIENĖ Kaunas University of Technology

DOI:

https://doi.org/10.5755/j01.ms.19.1.3831

Keywords:

woven fabric, structure, cotton, bamboo, laundering, chemical softener, seam slippage

Abstract

In the presented study the effect of laundering on the quality of sewn cotton and bamboo plain woven fabrics was investigated considering both the textile parameters and the type of chemical treatment. Quality parameters of sewn cotton and bamboo woven fabrics such as: fabric strength, seam strength and seam slippage at the moment of 4 mm seam opening were evaluated before and after washing with “Tide” washing powder without softeners or with softeners: “Surcare” and “Pflege Weicspuler”. There was also determined surface density, warp and weft densities as well as thicknesses under the pressures 0.625 kPa and 3.125 kPa, and calculated the comparative thickness that was considered as softness or porosity of fabrics.

Notwithstanding that both the investigated fabrics were cellulosic their behavior after laundering was different. Under the tested conditions, unwashed and laundered with or without chemical softeners cotton fabric didn’t demonstrate seam slippage. The seam slippage resistance of laundered without or with softener specimens of bamboo fabric was increased in respect to control fabric. The larger changes in seam efficiency and seam strength because of laundering were determined for bamboo woven fabric then for cotton fabric. They could be influenced by the higher changes in bamboo fabric’s structure. The highest difference between the structure parameters of both fabrics was determined for comparative thickness. It was significantly increased for cotton fabric and decreased for bamboo fabric after chemical softening comparing to untreated fabrics.

DOI: http://dx.doi.org/10.5755/j01.ms.19.1.3831

Downloads

Published

2013-03-19