Analysis of 3D Printed Diopside Scaffolds Properties for Tissue Engineering
AbstractDiopside exhibits favorable potential for bone repair on account of the good mechanical performance, bioactivity and biocompatibility. In this paper, diopside scaffolds with high pore interconnectivity were successfully fabricated by laser three-dimensional (3D) printing. The microstructure and mechanical performance of the diopside scaffolds were studied. The experimental analysis indicated that diopside particles gradually fused together until a dense structure was built with an energy density increasing in the range between 2.4 and 4.8 J·mm-2. Meanwhile, compressive strength and fracture toughness increased gradually from 5.96 ± 0.88 MPa to 10.87 ± 0.55 MPa. However, mechanical properties decreased due to the appearance of voids when energy density were 5.4 and 6 J·mm-2. Simulated body fluid (SBF) tests showed that apatite crystals formed on the diopside scaffolds surface, and the apatite crystals increased with soaking time. Cell culture tests indicated the scaffolds supported the adhesion and growth of MG-63 cells. The study suggested that diopside scaffolds fabricated by laser 3D printing are promising candidates for bone tissue engineering.
Copyright terms are indicated in the Republic of Lithuania Law on Copyright and Related Rights, Articles 4-37.
The copyright for articles in this journal are retained by the author(s), with first publication rights granted to the journal. By virtue of their appearance in this open access journal, articles are free to use with proper attribution in educational and other non-commercial settings.